Natural graphite flake is chemically treated to form Graphite Intercalation Compound. This intercalation compound is then rapidly heated to decomposition. The result is a rapid expansion of the panicle size. The bulk density of the yvorm-like graphite powders is about 0. 003g/cc. Then they are formed into graphite sheets by rolling.
Principal applications:
 Glands
 Gaskets used in flanges, covers of observation holes, level meters.
 Direct attach to the metal surfaces for gas phase sealing effectively.
 Especially the expanded graphite rolls can be used as a material for automatic producing lines. 
Specification of expanded graphite rolling

Item	Unit	Value
Tolerance of density	g/cm3	-0.06~+0.06
Tolerance of thickness	mm	-0.04~+0.04
Carbon content	%	99
Tensile strength	MPa	4.5
Compressibility	%	>40
Recovery	%	>10
Sulphur content	ppm	<1100
Chlorine content	ppm	<45
Temperature	°C	-200~+600

Rolling sheet size:

Density(g/cm3)	Length(m)	Width(mm)	Thickness(mm)
0.8(or) 1.0(or)1.1	30,50,80,or other size	<=1500 recommend use 1000mm	0.2~1.0 recommend use 0.2, 0.25,0.3,0.4,0.5,0.6,0.75,0.8mm

Special specification can be production for require.